Simple 162 Wedge Cut Test

peter

January 23, 2013 16:20

Here is a simple test video we created yesterday. It's the 162 Bushcrafter, out of S30V. We perform this test because it is a simple method of checking edge strength, and will identify issues like chipping, dulling, etc.
We always do a series of ten notch cuts, but that would have been a really long video. We found the 162 performed very well in this test.

Comments

23 comments

joekarp

January 23, 2013 16:28
Thanks Peter - not much hair left on your arm and with good ears I could hear the blade bite.

BTW - the moustache looks good. Wax On, Wax Off huh?
0
dj

January 23, 2013 16:39
These threads are a good idea on BM,s part .....
I can see where this is inspiring me to buy one of these knives .........LOL
0
theoneandonly

January 23, 2013 17:25
That was one of the ones I was considering, I guess this seals the deal

I think this once again proves why BM is at the top of their game. Great vid, any chance we can get one with the new tomahawk? I would love to see how those are tested
0
archer

January 23, 2013 19:04
Excellent!!
I'm impressed with the steel and the knife and this is the lowly S30V steel.
0
po

January 23, 2013 19:54
Thanks, Peter, this was extremely illuminating!

I have been harboring some doubts about S30V for hard use blades due to some reports about density and compression deformation. But if the 162 can perform like that with no edge degradation, that goes a long ways toward wiping those doubts away. And if anyone should know about the durability of S30V edges it would be Shane, as he's been using S30V on his extreme use models for a long time.

I wonder how how many dents you would have seen on the spine if you had hammered it with another piece of wood instead of a rubber malet.

Thanks for sharing this...it's a privilege.
0
peter

January 23, 2013 20:27
quote:

Originally posted by Po:

I wonder how how many dents you would have seen on the spine if you had hammered it with another piece of wood instead of a rubber malet.

Actually started off using a big hunk of Doug Fir to hammer on the spine. No damage to the blade, but the wood didn't last long. Switched to a thick chunk of Delrin round stock, didn't damage the spine at all either, but was comical looking and really loud during filming. I've yet to really be able to damage this knife, although I'm gonna keep trying. lol.
0
trailboss

January 23, 2013 20:37
quote:

Originally posted by Peter:

.... I've yet to really be able to damage this knife, although I'm gonna keep trying. lol.

Between the video and that statement, you've just about got me talked into one.
0
loonybin

January 24, 2013 00:39
Once I watched it on Chrome (I still can't get youtube videos to show up on Firefox), it cemented my decision to get this knife! If it can do that, then it will process deer from gutting to freezer with ease!
0
geocyclist

January 24, 2013 01:32
I sincerely cannot thank you enough. This sealed the deal for me on this knife. I had asked this very question on the forum earlier, how does S30V perform as in bushcrafting applications? It is a good steel for folders in EDC applications, but how does the edge hold up on hard use, especially since many fixed bush knives are 1095.

I would also be interested to see any type of test you do (video or empirical data) of 2 different steels of the same blade geometry.
0
bchan77

January 24, 2013 01:33
Peter, do you realize that when you show us your test video you are not only doing product testing, you are doing marketing as well?

I too have some misgivings about using S30V as a bushcraft knife -- I am leaning towards good old 1095 -- but your video has made me rethink about S30V. Keep those videos coming!
0
jonadz

January 24, 2013 02:51
Alright.... Sold! I'll deal with the green scales I guess! By the way, since you can no longer sell that one you tested with I'll gladly give it a new home with plenty of use!
0
deathofallthings

January 24, 2013 06:35
You know, I was looking hard into getting an ESEE 6... but now I'm thinking about a 162. I hadn't thought that S30v would be right for use like that, but I guess I was wrong. I just wish the 162 had a different style sheath.
0
acar

January 24, 2013 12:47
Excellent!
0
po

January 24, 2013 16:24
quote:

Originally posted by Peter:
...started off using a big hunk of Doug Fir to hammer on the spine...

Thanks, Peter. I've learned something about S30V here. It isn't just for <4" folders anymore.
0
mikeace

January 24, 2013 20:07
Yes, thanks for sharing that with us Peter.
0
thepunisher

January 25, 2013 19:01
nice vid and try.

why not chop without the mallet,as for choppers that is what we do.

i use a busse or esee to chop with?
0
sonnyc 2

January 25, 2013 23:00
I watched the video and instantly ordered one!
I can't believe that I just bought a fixed blade knife other than a Randall; but the test video sold me.
0
djsportland

January 27, 2013 21:05
Good stuff thanks!
0
mcm

January 29, 2013 10:02
Good job Peter!
0
minkeyman

February 05, 2013 17:20
Good vid!
0
peter

February 11, 2013 17:43
quote:

Originally posted by Geocyclist:
I sincerely cannot thank you enough. This sealed the deal for me on this knife. I had asked this very question on the forum earlier, how does S30V perform as in bushcrafting applications? It is a good steel for folders in EDC applications, but how does the edge hold up on hard use, especially since many fixed bush knives are 1095.

I would also be interested to see any type of test you do (video or empirical data) of 2 different steels of the same blade geometry.

Here is a discontinued product, the 158CSK. It is made from 1095 blade steel and has as close to the same edge geometry, thickness, and angle as I can get at this time. Thought you might like to see how it performed as well. enjoy.
0
zpstl321

March 10, 2013 23:57
I received my 162 on Friday and it is a great knife for sure! I've been playing with it all weekend.
0
geocyclist

March 12, 2013 02:10
Thanks Peter. The 158CSK was an interesting test. It really goes right through the wood. (or maybe you had your wheaties today)

Thanks for explaining a few days ago why you pry the wood chips out, to test the edge. I did not know you were doing it on purpose and just thought you were trying to get big chips out.
0